It's softer than 7075-t6 so technically it will wear faster but the 6061 will still suffice as long as it's properly anodized to surface harden. Most civilian owned firearms will never see a high enough round count for the aluminum type to make any difference.
If the 6061 is simply Cerakoted instead of anodized then that becomes a different story.