Paul Jacobsen
Member
Thats where I bought mine.....mic's out at .014 on my roll...perfect size.
gas check alumimun
- Thread starter mg34
- Start date
Thats where I bought mine.....mic's out at .014 on my roll...perfect size.
Had an order for copper sheet since July no happy ending yet
Euramax will only ship 4 coils at $125 per coil to a dealer. I have been waiting since July for Euromax to ship.
If you live in Alberta there are many companies that supply aluminum sheeting for pipelines.
Most of it is between .015-.016” thick. When I realised this , I procured about 50, full brand new sheets of this material. It works great!
Most of it is between .015-.016” thick. When I realised this , I procured about 50, full brand new sheets of this material. It works great!
I just used some aluminum edging for house siding. It measured out at .014-.016. A friend had it stashed away behind his shed from a job long ago. There wasn't much there but I got quite a few checks out of it. I just used my vise to flatten it out before cutting it into strips.
It might be worth looking up your local siding businesses and asking them if you can pick up their scraps.
It might be worth looking up your local siding businesses and asking them if you can pick up their scraps.
one problem with aluminium is the formation of oxide IIRC. If it forms on the gas check, it can cause issues as it is harder than steel. I have no experience in such things, but have done some reading in preparation of casting projectiles for my old Enfield .303
If any more knowledgeable person can confirm or deny this I would be interested
It is the reason I have avoided aluminium as a material for gas checks in my preparations. (I also haven't quite decided on which tool to make them, or whether I will just build one)
If any more knowledgeable person can confirm or deny this I would be interested
It is the reason I have avoided aluminium as a material for gas checks in my preparations. (I also haven't quite decided on which tool to make them, or whether I will just build one)one problem with aluminium is the formation of oxide IIRC. If it forms on the gas check, it can cause issues as it is harder than steel. I have no experience in such things, but have done some reading in preparation of casting projectiles for my old Enfield .303
If any more knowledgeable person can confirm or deny this I would be interested
Use epoxy coated aluminium flashing - no oxides and powder coat..
There are roles that are 12" x 20' minimum 4 roll order $425 CDN O.014" thick
Last edited:
thanks! so are you saying to powder coat the bullet afterwards? Or are you saying that there is no oxide or powder coat residue on the flasing? Sorry about the semantics game, but lets just assume that you are talking to a dummy (lol.. me)
My thought is that any coating on the flashing may be stripped off during the stress of the gas-check forming process.. is this not the case? Perhaps the coating is flexible enough to withstand the bending?
Thank you for the insight.. I like to always be learning.
Quote Originally Posted by bobbynewmark View Post
one problem with aluminium is the formation of oxide IIRC. If it forms on the gas check, it can cause issues as it is harder than steel. I have no experience in such things, but have done some reading in preparation of casting projectiles for my old Enfield .303
If any more knowledgeable person can confirm or deny this I would be interested It is the reason I have avoided aluminium as a material for gas checks in my preparations. (I also haven't quite decided on which tool to make them, or whether I will just build one)
Use epoxy coated aluminium flashing - no oxides and powder coat..
My thought is that any coating on the flashing may be stripped off during the stress of the gas-check forming process.. is this not the case? Perhaps the coating is flexible enough to withstand the bending?
Thank you for the insight.. I like to always be learning.
Quote Originally Posted by bobbynewmark View Post
one problem with aluminium is the formation of oxide IIRC. If it forms on the gas check, it can cause issues as it is harder than steel. I have no experience in such things, but have done some reading in preparation of casting projectiles for my old Enfield .303
If any more knowledgeable person can confirm or deny this I would be interested It is the reason I have avoided aluminium as a material for gas checks in my preparations. (I also haven't quite decided on which tool to make them, or whether I will just build one)
Use epoxy coated aluminium flashing - no oxides and powder coat..
Last edited:
gawd.. I hit reply instead of 'reply with quote'.. then tried to fix it and buggered it again.. My bad, I am middle aged with fat fingers
I recall women who said " I just washed my hair and now I can't do a thing with it!"
Well, due to a wish to comply with hygene standards I wash my hands many times a day and It is becoming hard to do anything with them....
I have made several thousand gas checks from the Freechex IIi tool using powder coated aluminium (0.014") The powder coat is tough stuff. It stays on the aluminium while being pushed through the die, and it is not damaged by resizing.
You can put your gas checks on the bullets before you powder coat them, or after.
I have done both - as long as the bullet is 0.001" or more over bore diameter accuracy really doesn't change. (The last issue of hand loader suggested two coats of powder coat may increase group size. There were not enough details on how he did the two coats and whether or not he ran the bullets through a sizer die, or possibly some other variable was at play. Most articles about casting (Mike Venturino excluded) in the gun mags only touch the surface of casting and cast bullet shooting.
The Pat Marlins gas check maker works - but it is not as slick as the freechex unit. Too bad Charlie Darnell faces some challenges in supply and sales. .
If you do make your own check maker, the slot in the die for the strip of flashing can be tailored to the thickness of the material you use.
The shank of the bullet where the check crimps on is usually 0.014" of an inch smaller than bullet diameter.
The real issue folks in rural places face is getting gas check material at a reasonable price.
I make a 0.225" gas check for a 37 grain NOE bullet. A $120 coil of aluminium or copper may out last my grandchildren and it is way more gas checks than I can ever get enough lead to cast the bullets for.